Introduction 

Inert alumina ceramic balls are widely used in petroleum, chemical industry, chemical fertilizer, natural gas, environmental protection and other industries, as the covering support materials and tower packing of catalyst in the reactor. It has the characteristics of high temperature and pressure resistance, low water absorption and stable chemical properties. It can withstand the corrosion of acid, alkali and other organic solvents, and can withstand the temperature change in the production process. Its main function is to increase gas or liquid distribution point, support and protect the active catalyst with low strength.

Product Name Company Ceramic Ball Alumina Ceramic Ball Alumina Ceramic Ball High Alumina Ceramic Ball Pure Alumina Ceramic Ball
AL2O3+SiO2 % >93 >92 >93 >94 >99
AL2O3 % 17-23 23-30 47-56 90-92 99
Fe2O3 % <1 <1 <1 <1 0.2
CaO % <0.5 <1.5 <2 <4 0.2
MgO % <0.5 <2.5 <0.5 <0.5 0.1
K2O+Na2O % <4 <4 <3.5 <4 >0.5
TiO2 % ------ <0.5 <0.1 <0.1 0.5
free Fe2O3 % ------ <0.1 <0.001 <0.001  
Water absorption rate % <0.5 <0.5 <2 <3 2.0-6.0
Bulk density g/cm3 1.2-1.4 1.35-1.45 1.8 1.9-2.0 2.0-2.2
Operating temperature ℃ >1300 >1400 1480 1760 ≥1700
Mohs hardness level 7 7 7 7 7.5
Acid resistance % ≥98 ≥98 ≥98 ≥98 ≥98
Alkali resistance % ≥80 ≥82 ≥85 ≥90 ≥95
compressive strength KN/Seed          

1/8"(3mm)

   0.34 0.37 0.45 0.5 0.55

1/4"(6mm)

   0.4 0.45 0.6 0.7 0.8
3/8"(10mm)   0.9 1 1.2 1.5 1.8
1/2"(13mm)   1.2 1.35-1.45 1.6 1.8 2
3/4"(19mm)   1.8 2 2.3 2.8 3.2
1"(25mm)   2.5 2.8 3.2 3.6 4
1-1/2"(38mm)   4 4.5 5 5.5 6
2"(50mm)   6 6.2 10 10.5 11
Note: the bulk density data is only for use and participation, not as the basis for acceptance.        

 

Specification and diameter tolerance

 

 

diameterΦ 3 6 8 10 13 16 20 25 30 38 50
Diameter tolerance ±1.0 ±1.5 ±2.0

 

Executive standard

Industrial ceramic ball inert ceramic ball (Hg / t3683.2-2014), chemical industry standard of the people's Republic of China.

" />
当前位置：产品中心>惰性氧化铝填料球

高铝填料球

销售热线：

产品介绍

     概述

    　　惰性氧化铝填料球广泛用于石油、化工、化肥、天然气及环保等行业，作为反应器内催化剂的覆盖支撑材料和塔填料。它具有耐高温高压，吸水率低，化学性能稳定的特点。能经受酸、碱及其他有机溶剂的腐蚀，并能经受生产过程中出现的温度变化。其主要作用是增加气体或液体分布点，支撑和保护强度不高的活性催化剂。

     性能

     

    品名 单位 普通瓷球 惰性氧化铝瓷球 中铝瓷球 高铝瓷球 纯铝瓷球
    AL2O3+SiO2 % >93 >92 >93 >94 >99
    AL2O3 % 17-23 23-30 47-56 90-92 99
    Fe2O3 % <1 <1 <1 <1 0.2
    CaO % <0.5 <1.5 <2 <4 0.2
    MgO % <0.5 <2.5 <0.5 <0.5 0.1
    K2O+Na2O % <4 <4 <3.5 <4 >0.5
    TiO2 % ------ <0.5 <0.1 <0.1 0.5
    游离Fe2O3 % ------ <0.1 <0.001 <0.001  
    吸水率 % <0.5 <0.5 <2 <3 2.0-6.0
    堆积密度 g/cm3 1.3-1.4 1.35-1.45 1.8 1.9-2.0 2.0-2.2
    操作温度 ℃ >1300 >1400 1480 1760 ≥1700
    莫氏硬度 级 7 7 7 7 7.5
    耐酸度 % ≥98 ≥98 ≥98 ≥98 ≥98
    耐碱度 % ≥80 ≥82 ≥85 ≥90 ≥95
    抗压强度 KN/颗          

    1/8"(3mm)

    		   0.34 0.37 0.45 0.5 0.55

    1/4"(6mm)

    		   0.4 0.45 0.6 0.7 0.8
    3/8"(10mm)   0.9 1 1.2 1.5 1.8
    1/2"(13mm)   1.2 1.35-1.45 1.6 1.8 2
    3/4"(19mm)   1.8 2 2.3 2.8 3.2
    1"(25mm)   2.5 2.8 3.2 3.6 4
    1-1/2"(38mm)   4 4.5 5 5.5 6
    2"(50mm)   6 6.2 10 10.5 11
    注:堆积密度数据仅供使用参与,不作为验收依据。        


     规格及直径允差

     

     

    直径Φ 3 6 8 10 13 16 20 25 30 38 50
    直径允差 ±1.0 ±1.5 ±2.0

     

     

     执行标准

          中华人民共和国化工行业标准HG/T3683.2-2014《工业瓷球-惰性瓷球》。